Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Dense Zircon Block
- Related Products
- Dense Zircon Block
- High Dense Zircon Block
- Zircon Brick
Apparent Porosity: ≤18%
Bulk Density: ≥3.65 g/cm3
Cold Crushing Strength: ≥100Mpa
0.2Mpa Refractoriness Under Load T0.6 : ≥1650℃
Pyrometric Cone Equivalent S.C. SK : 40
Reversible Thermal Expansion 1000℃: 0.5%
Dense zircon brick ZS-65 is a kind of fire brick. The zircon content of it is equal to or greater than 65 percent. It possesses many advantages as high bulk density, low apparent porosity, high cold crushing strength and high refractoriness under load. It is widely used in glass industry and metallurgical industry.
▶ Applications:
Dense Zircon brick is widely used in the upper area of flame space and frequent thermal shock region of alkali-free or low-alkali glass, sodium-calcium glass, boron-silicate glass, lead glass and other technical glass melting furnace. It can be also used in transition region between up roof silica brick and fusion zirconia-corundum brick or fusion zirconia-mullite brick, transition region between silica brick and magnesia brick, crown, burner, thermal couple, peep hole, secondary layer of melting bottom and back lining. In addition, it is also applied as the ladle lining for metallurgical industry.
▶ The main applications:
It is mainly applied in the neutral course in tank superstructure and sealing course in tank bottom.
▶ Specifications:
◆ High density;
◆ Superior quality;
◆ Accurate size tolerance;
◆ Luster apperance.
▶ Advantages:
◆ High bulk density;
◆ Low apparent porosity;
◆ High cold crushing strength;
◆ High refractoriness under load.
| Item | ZS-65 |
| ZrO2 (%) | ≥65 |
| SiO2 (%) | ≤33 |
| Fe2O3 (%) | ≤0.5 |
| Apparent Porosity (%) | ≤18 |
| Bulk Density (g/cm3) | ≥3.65 |
| Cold Crushing Strength (Mpa) | ≥100 |
| 0.2Mpa Refractoriness Under Load T0.6 (℃) | ≥1650 |
| Pyrometric Cone Equivalent S.C. SK | 40 |
| Reversible Thermal Expansion 1000℃ (%) | 0.5 |