Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Fused Cast AZS TY-AZS36
- Related Products
- Fused Cast AZS TY-AZS33
- Fused Cast AZS TY-AZS36
- Fused Cast AZS TY-AZS41
Bulk density: ≥3.85g/cm3
Apparent Porosity: ≤1.0%
Cold Crushing Strength Mpa: ≥300
Exudation Temperature of Glass Phase: ≥1400
Bubble Separation Ratio(1300℃×10h): ≤1.4
Anti-corrosion rate of glass liquid 1500℃×36h (mm/24h)%:
►TY- AZS36 Shapes and sizes:
This product is only available for straight brick.
Application: mainly used for side walls of flame furnaces with embedded melter bottoms, for total security with average pulls and campaign lengths, and superstructures, front wall, back wall, top crown in glass melting furnace.
►Advantages:
◆ Compact microstructure;
◆ Good erosion resistibility to molten glass;
◆ Good thermal shock resistibility;
◆ Barely rendering blister.
►Application:
Mainly used for sidewalls, doghouses, throat, bottom budding, Dam blocks, electric block corners.
Fused Cast AZS are the most widely used materials both in glass contact and superstructure of glass melting furnaces.
The products have passed the ISO international certified, are made of high pure material, fired at high temperature by advanced technology, with the advantages of high strength, high compression resistance, good thermal shock resistance, good performance in high temperature, good thermal conductivity, good erosion resistance and so on. Widely be used for linings of furnace in industries.
| Item | Behaviors | |
| TY-AZS36 | ||
| Chemical Composition | Al2O3 | ≥49.00 |
| ZrO2 | ≥35.50 | |
| SiO2 | ≤13.50 | |
| Na2O+K2O | ≤1.35 | |
| Bulk density (g/cm3) | ≥3.85 | |
| Apparent Porosity (%) | ≤1.0 | |
| Cold Crushing Strength Mpa | ≥300 | |
| Exudation Temperature of Glass Phase | ≥1400 | |
| Bubble Separation Ratio(1300℃×10h) | ≤1.4 | |
| Anti-corrosion rate of glass liquid 1500℃×36h (mm/24h)% | ≤1.3 | |
| Apparent density (g/cm3) | PT(RN RC N) | ≥3.50 |
| ZWS(RR EVF EC ENC) | ≥3.70 | |
| WS( RT VF EPIC FVP DCL) | ≥3.80 | |
Need more information? Drop us a line
For more information on any of our products please get in touch using the form below. One of our sales team will respond to your enquiry as soon as possible.