Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Magnesia Ferrum Spinel Brick
- Related Products
- Magnesia Brick
- Magnesia Chrome Brick
- Magnesia Carbon Brick
- Magnesia Zirconia Brick
Item: Synthetic Magnesia Ferrum Alumina Spinel Brick
Apparent Porosity: 17%
Cold Crushing Strength: 45 Mpa
Refractoriness under load: 1700 (0.2Mpa ℃)
Bulk Density: 3.00 g/cm3
Thermal Shock Resistance: 5 (1100℃ water cooling, times)
▶ Specifications:
Magnesia Ferrum Spinel Brick and synthetic magnesia ferrum alumina spinel brick are made of high purified magnesia clinker and ferrum alumina spinel clinker at strictly controlled temperature and sintered atmosphere, which enables the product to have good flexibility and temperature vibration.
▶ Application:
The performances of attaching kiln wall and corrosion resistance are better good quality magnesia chrome brick. The product is update product for lining of large dry cement rotary kilns.
| Item | Behaviors | ||
| Magnesia Ferrum Alumina Spinel Brick | |||
| TY-MFA80 | TY-MFA75 | ||
| Chemical Composition (%) | MgO ≥ | 83 | 82 |
| Al2O3 ≤ | 3-6 | 4-7 | |
| Fe2O3 | 5-8 | 5-8 | |
| Apparent Porosity (%) | 17 | 17 | |
| Cold Crushing Strength (Mpa) | 45 | 45 | |
| Refractoriness under load 0.2Mpa (℃) | 1700 | 1680 | |
| Bulk Density (g/cm3) | 3.00 | 2.98 | |
| Thermal Shock Resistance (1100℃ water cooling, times) | 5 | 5 | |