Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Synthetic Magnesia Olivine Brick
Item: Synthetic Magnesia Olivine Brick
Apparent Porosity: 20%
Bulk Density: 2.7 g/cm3
Cold Crushing Strength: 35 Mpa
0.2Mpa Refractoriness Under Load T0.6: 1650℃
Thermal shock resistance: 10 (950℃ air cooling ,times)
▶ Specification:
Synthetic magnesia olivine brick is neutral refractories with sintered olivine , serpentine and periclase as main phase .It has better alkaline slag leaching resistance.
▶ Application:
It is a kind of environmentally friendly product and a substitute for magnesia chrome brick used in glass furnace .The product has been successfully used in glass kilns at home and abroad for many years.
| Item | Behaviors | ||
| Synthetic Magnesia Olivine Brick | |||
| TY-MO-60 | TY-MO-50 | ||
| Chemical composition | MgO (%) | 60 | 50 |
| SiO2 (%) | 20 | 30 | |
| Apparent Porosity (%) | 20 | 20 | |
| Bulk Density (g/cm3) | 2.7 | 2.65 | |
| Cold Crushing Strength (Mpa) | 35 | 35 | |
| 0.2Mpa Refractoriness Under Load T0.6 ℃ | 1650 | 1620 | |
| Thermal shock resistance (950℃ air cooling ,times) | 10 | 10 | |