Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Magnesia Alumina Spinel Brick
- Related Products
- Magnesia Brick
- Magnesia Chrome Brick
- Magnesia Carbon Brick
- Magnesia Zirconia Brick
Item : Magnesia Alumina Spinel Brick
Apparent Porosity: 18%
Cold Crushing Strength: 40 Mpa
Refractoriness under load: 1620 (T0.6℃)
Bulk Density: 2.9 g/cm3
Thermal Shock Resistance: 6 (1100℃ water cooling, times)
▶ Specifications:
◆ High refractoriness.
◆ High resistance to corrosion.
◆ Excellent thermal shock resistance.
It is a kind of alkaline refractory product with perriclase as main phase magnesia alumina spinel clinker as basic material .The product has such characteristics as good temperature vibration, good strength and volume stability in high temperature.
▶ Application:
Magnesia Alumina Spinel Brick is widely used in transition zone of cement rotary kilns, glass tank regenerators and lime kilns.
| Item | Behaviors | |||
| Magnesia Alumina Spinel Brick | ||||
| TY-MA5 | TY-MA10 | TY-MA15 | ||
| Chemical composition | MgO (%) | 85 | 80 | 80 |
| Al2O3 (%) | 5-7 | 8-10 | 15-17 | |
| Apparent Porosity (%) | 18 | 18 | 17 | |
| Cold Crushing Strength (Mpa) | 40 | 40 | 40 | |
| Refractoriness under load T0.6 ℃ | 1620 | 1650 | 1650 | |
| Bulk Density (g/cm3) | 2.9 | 2.9 | 2.9 | |
| Thermal Shock Resistance (1100℃ water cooling, times) | 6 | 8 | 10 | |