Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Magnesia Zirconia Brick
- Related Products
- Magnesia Brick
- Magnesia Chrome Brick
- Magnesia Carbon Brick
- Magnesia Zirconia Brick
Item : Magnesia Zircon Brick
Apparent Porosity: ≤19%
Bulk Density : ≥3.95 g/cm3
Cold Crushing Strength : ≥50 MPa
Refractoriness Under Load: ≥1600℃
Thermal Shock Resistance: ≥10 (950-wind cold)
▶ Specifications:
◆ alkali resistance;
◆ slag corrosion resistance;
◆ spalling resistance;
◆ high-temperature resistance.
▶ Descriptions:
The product is composed of fused magnesia sand and zircon sand and it belongs to alkaline material. This product has high density (Bulk density) is greater than 3.08(g/cm3). It also resists alkaline atmosphere erosion and alkaline slag erosion and widely used in glass furnace, regenerative chamber, cement kiln, steel-making electric furnace and non-ferrous metal metallurgy.
▶ Application:
Magnesia Zircon Brick is used for regenerator of glass furnace.
| Item | Magnesia-Zircon Brick | ||
| TY-MZ8 | TY-MZ10 | TY-MZ13 | |
| MgO (%) ≥ | 80 | 75 | 70 |
| ZrO2 (%) ≥ | 8 | 10 | 13 |
| Apparent Porosity (%) ≤ | 19 | 18 | 18 |
| Bulk Density (g/cm3) ≥ | 3.95 | 3.00 | 3.05 |
| Cold Crushing Strength (MPa) ≥ | 50 | 45 | 40 |
| Refractoriness Under Load (℃) ≥ | 1600 | 1550 | 1600 |
| Thermal Shock Resistance (950-wind cold) ≥ | 10 | 10 | 10 |
Need more information? Drop us a line