Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Fused Chrome Corundum Block
- Related Products
- Fused Corundum Block
- Fused Chrome Corundum Block
Item :Chrome corundum block
Apparent Prosity: ≤15 (%)
Bulk Density: ≥3.25 g/cm3
Cold Crushing Strength: ≥180 Mpa
Refractoriness: ≥1900 ℃
0.2Mpa Refractoriness Under Load T0.6: ≥1680℃
▶ Fused chrome corundum block:
Due to its good chemical stability, high fire resistance, big intensity and good high temperature performance, it is a new top-grade refractory material with high erosion resistant. It is widely used for liner of high-temperature kilns required for steel, building material, non-ferrous smelt industry, light industry and chemical industry.
▶ Application:
Fused chrome corundum block is mainly used in areas that require high abrasion and temperature resistance, such as gliding rail bricks in steel pusher metallurgical furnaces, the tapping platform (tapping spout) style walking beam furnaces, and also as the interior for destructors, In the linings of carbon soot furnace and copper smeling furnace tapping platform of rolling mill furnace, reheating furnace skid rail.
| Item | Behaviors | |
| TY-G92-Cr | ||
| Chemical Composition (%) | Al2O3 | ≥92 |
| SiO2 | ≤1.0 | |
| Fe2O3 | ≤0.3 | |
| CaO | ≤1.2 | |
| Na2O | - | |
| ZrO2 | ≥3 | |
| Cr2O3 | ≥3 | |
| Apparent Prosity (%) | ≤15 | |
| Bulk Density (g/cm3) | ≥3.25 | |
| Cold Crushing Strength (Mpa) | ≥180 | |
| Modulus of Rupture at High Temperature 1250℃ (Mpa) |
≥9.5 | |
| Refractoriness (℃) | ≥1900 | |
| 0.2Mpa Refractoriness Under Load T0.6 (℃) | ≥1680 | |
| Reheat liner change 1600℃×3h (%) | ≤±0.2 | |
Need more information? Drop us a line