High Quality Silica Brick

High Quality Silica Brick
High Quality Silica Brick
High Quality Silica Brick
High Quality Silica Brick
Overview

Refractoriness :1710 ℃

Apparent Porosity:≤21 %

Bulk Density :≥1.8 g/cm3

True Density:≤2.34 g/cm3

Cold Crushing Strength :≥35 Mpa

0.2Mpa Refractoriness Under Load T0.6 ℃:≥1680

Feature

A brief introduction of silica brick

Silica brick is a kind of acid refractory mainly made from tridymite, cristobalite and a small amount of residual quartz as well as glass phase. The raw material is natural silica sand whose SiO2 content should be more than 96%. The higher SiO2 content in silica sand, the higher temperature silica bricks resist. Silica bricks are used in the roof and superstructure of glass melting tanks as well as for hot repairs.

Our silica brick  advantages

--Adopts high quality silica and advanced technology, our silica bricks enjoy the advantages of high purity, long service life, good thermal conductivity, high refractoriness under load, and good creep resistance.

--In addition, it has accurate size tolerance, pure color and luster appearance.

--Because of the good thermal shock resistance of silica brick, it is mainly used in the continuous operating furnace.

--Supporting the use of other high quality refractories, our silica brick can extent the service life of float glass furnace to 8 years and double the service life of bottle glass furnace.

Applications

The silica brick can be widely used in coke oven, hot blast furnace, glass furnace and carbon furnace. In glass industry, it is mainly employed to build the doghouse crown, suspended wall of channel, top crown and inlet sealing. In detail, silica bricks plays  the following role in different fields:

--being the partition walls in coke oven carbonization and burning chamber;

--metallurgy industry: used as refractories for steel making open hearth regenerator, slag pocket, soaking pit;

--arch crown and other weight bearing areas in ceramic kilns, hot blast furnace and acid open hearth;

--worked as building checker chamber, chute, combustion chamber, coking chamber and furnace arch in glass melting furnaces
High Quality Silica Brick


 

Technical Data
Item BG-96A BG-96B
Chemical composition SiO2 ≥96 ≥96
  Fe2O3 ≤0.8 ≤0.7
  Al2O3+TiO2+R2O ≤0.5 ≤0.7
Refractoriness ℃ 1710 1710
Apparent Porosity% ≤21 ≤21
Bulk Density g/cm3 ≥1.8 ≥1.8
True Density,g/cm3 ≤2.34 ≤2.34
Cold Crushing Strength Mpa ≥35 ≥35
0.2Mpa Refractoriness Under Load T0.6 ℃ ≥1680 ≥1680
Permanent Linear Change On Reheating (%)1500℃X2h 0~+0.3 0~+0.3
20-1000℃ Thermal Expansich10-6/℃ 1.25 1.25
Thermal Conductivity (W/MK) 1000℃ 1.44 1.44

Need more information? Drop us a line

For more information on any of our products please get in touch using the form below. One of our sales team will respond to your enquiry as soon as possible.