Fused Cast AZS Block
AZS Casting Type
AZS Ramming Materials
Fused Cast AZS TY-AZS41
Fused Cast AZS TY-AZS36
Fused Cast AZS TY-AZS33
Fused Cast Alumina Block
Fused cast Alumina Block TY-H
Fused cast Alumina Block TY-A
Fused cast Alumina Block TY-M
Fused Cast High Zirconia Block
Fused Cast Skid Rail Block
Silica brick
Magnesia Series Brick
Bonded Refractory Block
High alumina And Fire clay bricks
Insulation Series Brick
Ceramic Fiber Products
- 0086 371 63838939
- 0086 371 63835539
- sales@sunriserefr.com
- tkfanyi
- No.36 Fengchan Road, Zhengzhou City
Big Fireclay Bottom Blocks
- Related Products
- Big Fireclay Bottom Blocks
Item: Behaviors
Refractoriness: ≥1750℃
Bulk Density: ≥2.3 g/cm3
Apparent Porosity: ＜18%
Cold Crushing Strength: ＞50 Mpa
0.2Mpa Softening Temp Under Load: ≥1450℃
Using big vibrating table and adopting special castables, the company produces furnace large fireclay blocks with vibrate moulding technology. The physical and chemical properties and appearance of the blocks have exceeded the national standards. The resistant ability to molten glass of the products is better than that of fanditional casting process products and ramming products. The products are especially suitable to build the bottom of furnace, cooling and working end side wall of glass furnace.
▶ Specifications:
◆ Low permanent linear change on reheating;
◆ High dense structure;
◆ Good Thermal Shock Stability.
▶ Advantages:
◆ Good wear-resistance;
◆ Corrosion-resistant;
◆ Various shapes;
◆ High quality.
| Item | Behaviors | |
| Physical properties | Refractoriness (℃) | ≥1750 |
| Bulk Density (g/cm3) | ≥2.3 | |
| Apparent Porosity (%) | ＜18 | |
| Cold Crushing Strength (Mpa) | ＞50 | |
| 0.2Mpa Softening Temp Under Load (℃) | ≥1450 | |
| 1400℃x2h Permanent Linear Change (%) | ±0.2 | |
| Chemical Composition (%) | Al2O3 | ≥40 |
| Fe2O3 | ≤1.5 | |
Need more information? Drop us a line
For more information on any of our products please get in touch using the form below. One of our sales team will respond to your enquiry as soon as possible.